In Our Element: How Do You Clean Copper Beryllium?

In Our Element Video Series
8 min
Mike Gedeon, Customer Technical Services Manager


At room temperature, copper-beryllium forms a thin tarnish layer. At the higher temperatures associated with heat treating, heavy oxide layers can occur. These oxides can interfere with subsequent surface operations such as plating or soldering, which is why it is critical to clean the material to remove the oxides. But where do you start? Below, I will describe how the oxides form and how they can be removed using various techniques.  


Let’s start with oxide formation. Heat treating copper-beryllium parts produces an oxide film on their surfaces. The surface oxide is a mixture of beryllium oxide (BeO) and several copper oxides. The composition and thickness of this film is dependent on temperature and furnace atmosphere. It is important to remember that beryllium has a great affinity for oxygen and since beryllium oxide is not reduced by hydrogen, there is no heat treating atmosphere that will provide a surface free of beryllium oxide. How much oxide, what type of oxide and ease of cleaning does depend on heat treat conditions and procedures. Heat treating a “clean” surface, free of oils and other contaminants, simplifies cleaning after heat treatment, and should be standard operating practice in any event. 

The composition and thickness of oxide films formed on the various copper beryllium alloys will vary somewhat depending on the beryllium content of the particular alloy, but the behavior of our copper beryllium Alloy 25 (C17200) is typical. In nominal nitrogen atmospheres (with or without hydrogen) the degree of BeO formation on heat treated Alloy 25 is dependent on temperature, as is the total thickness of the oxide scale. At 700°F and above, the outermost layer is primarily BeO while below this temperature (600°F and 500°F) the outer scale is composed of a mixture of BeO and copper oxides, typically 30% BeO at 600°F and 20% BeO at 500°F. These observations are important from a cleaning standpoint since BeO is not readily attacked by acids. Not only is the oxide thinner at the lower temperatures, but its composition makes it more readily soluble in pickling baths. Time at temperature and type of “inert” atmosphere are also factors in film thickness and composition. 

In a typical age hardening heat treatment (two hours at 600°F) carried out in an “inert” atmosphere, a film thickness of about 300-800 Å can be expected on alloy C17200. Under solution annealing conditions (1450°F), the film can reach as much as 1000-2000 Å.


These oxide films must be removed prior to stamping, plating, soldering, brazing or welding. The most difficult to remove are the thicker ones composed primarily of beryllium oxide, such as those formed in solution annealing operations. Fortunately, most solution annealing operations are performed only by the copper beryllium producers who have the necessary equipment and expertise to be able to supply an “oxide free” strip to the component manufacturer. Such films require hot, concentrated caustic pretreatment to render them acid soluble. 

The component manufacturer, however, frequently age hardens the copper-beryllium after stamping and must clean the parts before subsequent processing. There are many acid combinations which can be used, but those proven most successful in removing films containing beryllium oxide are sulfuric/peroxide (20% H2SO4, 3% H2O2, 125°F) and phosphoric/nitric/acetic (PNA) (38% H3PO4, 2% HNO3, 60% acetic acid, 160°F). Nitric acid alone does not do an adequate job of removing BeO films unless these films are pretreated in hot, concentrated caustic (50-60% NaOH, 265°F). 

There are significant differences inherent in the use of these acids for pickling copper beryllium. I will discuss these in following paragraphs, but a note of caution is advised when dealing with any copper alloy containing lead, such as our Alloy M25 (C17300). Nitric acid or PNA is used rather than a sulfuric acid system because of the insolubility of lead sulfate. Also, fluoboric acid (10-25% at room temperature) is frequently used as a preplating acid dip for leaded alloys following alkaline cleaning. 

Incidentally, a cyanide copper strike is also recommended in the plating procedure as an additional guarantee for good adhesion on any copper alloy, but it is considered essential for leaded alloys. The cyanide strike is a cleaning and activating step.

It has been reported that with alloys containing beryllium, care must be taken to prevent the possibility of cyanide degradation of the substrate by too much exposure to cyanide containing solutions. This can lead to difficulties in adhesion but is rather easily avoided by omitting cyanide dips or soaks (but not necessarily cyanide strikes) prior to plating.

Now let’s discuss the acid combinations that can be used. 

Sulfuric Acid/Hydrogen Peroxide To Clean Copper Beryllium

The sulfuric/peroxide system has the advantages of easy control and ease of treatment of waste liquors. The pickling action on copper-beryllium is gentle with no noxious fumes generated, but there may be some entrainment of sulfuric acid vapors in a fume exhaust system. The sulfuric/ peroxide bath is what is known as a “bright dip” and leaves the surface with a bright, matte finish. A cold water rinse should be used with this process. The rate of reaction is controlled by hydrogen peroxide (H202) content and temperature. Sulfuric acid can range from 10 to 20 volume percent and has little effect on reaction rate. Dissolved copper can be removed from the pickle liquor by cooling to 60°F or so to allow CuSO4~ 5H2O to crystallize out of solution. The acid can be reused indefinitely. The limited solubility of copper sulfate is sometimes a liability if provisions are not made to properly control the copper ion concentration in the pickle liquor. Hydrogen peroxide in contact with dissolved oxygen must be stabilized or replenished to prevent rapid deterioration of the oxidizing power of the bath. Many proprietary cleaners that are based on the sulfuric/peroxide system contain the proper stabilizers. 

Nitric Acid System To Clean Copper Beryllium

The nitric acid system is somewhat cheaper, reaction rates can be varied over a very large range, and the surface finish achieved is bright and shiny, not matte. The disadvantages are the evolution of noxious fumes, the greater difficulty in controlling reaction rates, and waste disposal problems. The fumes can be controlled with the addition of urea to the nitric acid bath (1-2 ounces/gallon), but this complicates control. 

Reaction rate is dependent on the concentration of acid, urea and copper ion and on temperature. Temperature control is more difficult with urea additions, since the reaction becomes much more exothermic. More gas is evolved with urea also, which can cause foaming problems if urea concentration gets too high. Urea is not easily analyzed in the bath, but this generally doesn't present a problem since 0.5 pound urea is used up for each 1 pound of copper dissolved, and brown fumes of NO2 become apparent at concentrations below 1 ounce/gallon of urea. Many production facilities use nitric acid pickling without urea, but good fume removal must be provided. Copper is very soluble in the nitric acid solution, and good pickling can be maintained at concentrations as high as 150 grams/liter. A cold water rinse should be used. It is sometimes beneficial to use a dilute acid rinse (cold) before final rinsing to minimize staining. One to three percent HNO3 is used. 

Phosphoric/Nitric/Acetic Acids Approach to Cleaning Copper Beryllium

The phosphoric/nitric/acetic (PNA) system is a “bright dip,” which also polishes the surface, leaving it shiny and generally smoother (lower Ra) than before etching. A hot water rinse gives a better-looking surface than cold. Concentrations of the three acids can be varied, but less nitric makes the reaction more controllable. Concentrations of 38% H3PO4, 2% HNO3, and 60% acetic at 160°F are ideal for cleaning copper beryllium. Waste disposal may be a problem with this system used on a large scale because of the phosphate ion, as well as the copper ion. 


In any acid cleaning or pickling operation, the surface of the metal will be rendered more uniform if it is free of passivated areas beforehand, or quickly becomes so. Generally, this means that the surface should be as free as possible of oils, greases, carbonaceous matter and other "soils". This can be best achieved by the use of a good alkaline cleaner prior to acid pickling. If the cleaned surface is not to be immediately plated or soldered, precautions should be taken to prevent tarnishing during storage. Benzotriazole (BTA) is commonly used as a stain inhibitor for copper alloys. The BTA film provides shelf life protection for up to a year as long as the film is not damaged or condensed moisture is not allowed to condense on it. This film can also withstand temperatures up to 300°F before vaporizing. 


Copper beryllium alloys can be readily electroplated, soldered, welded or brazed, but extra care should be taken in cleaning heat treated alloys to ensure removal of oxide films. This can be accomplished by the use of a hot alkaline cleaner (cathodic or soak) followed by a mildly etching acid such as those described above.

Learn more about our high-strength and high-conductivity copper-beryllium alloys on our website.

Thanks for joining me for another edition of In Our Element. For ongoing industry updates, connect with me on LinkedIn.  

Health and Safety

Processing beryllium-containing alloys poses a health risk if safe practices are not followed.  Inhalation of airborne beryllium can cause serious lung diseases in some individuals.  Occupational safety and health regulatory agencies worldwide have set mandatory limits on occupational respiratory exposures.  Read and follow the guidance in the Safety Data Sheet (SDS) before working with this material.  The SDS and additional important beryllium health and safety information and guidance can be found at and

For questions on safe practices for beryllium-containing alloys, contact the Materion Product Stewardship Group at +1.800.862.4118 or contact us by email at


Search For: